In this work tensile strength, fatigue resistance and fracture toughness of two electroslag remelted (ESR) tool steels and of 33CrMoV12 ESR steel (both in quenched and tempered condition, as well as nitrided condition) were evaluated. The role of hardness, residual stresses and inclusion sizes on the fatigue behavior was investigated. Tool steels have a tensile strength between about 1900 and 2300 MPa, fracture toughness between 35 and 33 MPa root m, while fatigue strength ranges between 725 and 992 MPa. The tensile strength and fracture toughness of the 33CrMoV12 ESR are, respectively, 1365 MPa and about 150 MPa root m. Nitriding induces a significant increase in fatigue strength from 560 to 980 MPa. These results highlight that appropriate ESR tool steels could replace nitrided steels.
Ceschini, L., Morri, A., Morri, A., Messieri, S. (2018). Replacement of Nitrided 33CrMoV Steel with ESR Hot Work Tool Steels for Motorsport Applications: Microstructural and Fatigue Characterization. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 27(8), 3920-3931 [10.1007/s11665-018-3481-9].
Replacement of Nitrided 33CrMoV Steel with ESR Hot Work Tool Steels for Motorsport Applications: Microstructural and Fatigue Characterization
Ceschini, Lorella;Morri, Andrea;Morri, Alessandro
;MESSIERI, SIMONE
2018
Abstract
In this work tensile strength, fatigue resistance and fracture toughness of two electroslag remelted (ESR) tool steels and of 33CrMoV12 ESR steel (both in quenched and tempered condition, as well as nitrided condition) were evaluated. The role of hardness, residual stresses and inclusion sizes on the fatigue behavior was investigated. Tool steels have a tensile strength between about 1900 and 2300 MPa, fracture toughness between 35 and 33 MPa root m, while fatigue strength ranges between 725 and 992 MPa. The tensile strength and fracture toughness of the 33CrMoV12 ESR are, respectively, 1365 MPa and about 150 MPa root m. Nitriding induces a significant increase in fatigue strength from 560 to 980 MPa. These results highlight that appropriate ESR tool steels could replace nitrided steels.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.