Cyclability features of an all solid-state lithium polybithiophene battery with PEO20LiClO4 polymer electrolyte was investigated at 70°C working temperature. Although the capacity values of the solid device are lower than those of the comparable one with liquid electrolyte, the cyclability performances are promising and the cycle life is satisfactory. The shelf-life of the solid battery was also investigated. The self-discharge rate is fast at 70°C but is not appreciable at room temperature. © 1990.
Polybithiophene as positive electrode in solid-state polyethylene oxide-LiClO4 lithium rechargeable battery / Arbizzani C.; Mastragostino M.. - In: ELECTROCHIMICA ACTA. - ISSN 0013-4686. - STAMPA. - 35:1(1990), pp. 251-254. [10.1016/0013-4686(90)85066-V]
Polybithiophene as positive electrode in solid-state polyethylene oxide-LiClO4 lithium rechargeable battery
Arbizzani C.Primo
Investigation
;Mastragostino M.
1990
Abstract
Cyclability features of an all solid-state lithium polybithiophene battery with PEO20LiClO4 polymer electrolyte was investigated at 70°C working temperature. Although the capacity values of the solid device are lower than those of the comparable one with liquid electrolyte, the cyclability performances are promising and the cycle life is satisfactory. The shelf-life of the solid battery was also investigated. The self-discharge rate is fast at 70°C but is not appreciable at room temperature. © 1990.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.