IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishThe results of a comparative analysis performed on specimens of nanostructured epoxy resins obtained by different boehmite filler concentrations are reported in this paper. The specimens were prepared by dispersion of boehmite nanoparticles into a cycloaliphatic epoxy resin cross linked under UV. Photopolymerization process was followed by RT-FTIR and the properties of uv-cured films investigated. Dielectric properties, in particular space charge accumulation, are measured as a function of nanofiller content. Results indicate that space charge build up and charge mobility are affected largely by filler content. Concentrations of nanofiller of 5–7 wt % show significant decrease of the space charge with respect to the base-epoxy resin and an increased mobility of negative carriers.
| Titolo: | Epoxy-bohemite nanocomposites as new insulating materials |
| Autore/i: | M. Sangermano; F. Deorsola; FABIANI, DAVIDE; MONTANARI, GIAN CARLO; G. Rizza |
| Autore/i Unibo: | |
| Anno: | 2009 |
| Rivista: | |
| Digital Object Identifier (DOI): | http://dx.doi.org/10.1002/app.30799 |
| Abstract: | The results of a comparative analysis performed on specimens of nanostructured epoxy resins obtained by different boehmite filler concentrations are reported in this paper. The specimens were prepared by dispersion of boehmite nanoparticles into a cycloaliphatic epoxy resin cross linked under UV. Photopolymerization process was followed by RT-FTIR and the properties of uv-cured films investigated. Dielectric properties, in particular space charge accumulation, are measured as a function of nanofiller content. Results indicate that space charge build up and charge mobility are affected largely by filler content. Concentrations of nanofiller of 5–7 wt % show significant decrease of the space charge with respect to the base-epoxy resin and an increased mobility of negative carriers. |