Comparison between hydrofluoric acid and single-component primer as conditioners on resin cement adhesion to lithium silicate and lithium disilicate glass ceramics

This study aimed at evaluating the effects of different surface conditionings on the microshear bond strength (µSBS) of a self-adhesive resin cement to VITA Suprinity (ZLS) and IPS e.max CAD (LD). Three surface conditioning protocols were performed on ZLS and LD before luting with a self-adhesive resin cement (RelyX Unicem 2, RXU): hydrofluoric acid (HF), HF + silane (HF + S), or Monobond Etch & Prime (EP). In each group, 15 cylindrical buildups of RXU were prepared on five milled bars and submitted to a µSBS test. Data were statistically analyzed with two-way ANOVA and Tukey’s post hoc test (p < 0.05). Failure modes were recorded and classified as adhesive, mixed, cohesive in resin, or ceramic, and statistically analyzed with Fisher’s exact test (p = 0.05). One additional bar per group was used for the morphological characterization of the conditioned surface by means of SEM. The material per se did not significantly influence adhesion (p = 0.744). Conditioning protocol was a significant factor: EP yielded significantly higher μSBS than HF (p = 0.005), while no significant differences emerged between EP and HF + S (p = 0.107), or HF + S and HF (p = 0.387). The material-conditioning protocol interaction was not statistically significant (p = 0.109). Significant intergroup differences were found in distribution of failure modes: mixed failures were predominant in the ZLS/EP group, while the other groups showed a prevalence of adhesive failures. The self-etching primer showed promising results in terms of immediate bond strength of a self-adhesive resin cement to lithium-silica-based glass ceramics, suggesting its alternative use to hydrofluoric acid and silane conditioning protocols.