Role of hydrodynamics, li+ addition and transformation kinetics on the formation of plate-like {001} calcite crystals

Plate-like calcite crystals with expressed unstable {001} planes are interesting research model for investigations of interfacial interactions of different additive molecules, but also the crystal growth mechanisms. The aim of this study is to reproducibly prepare a significant amount of well-defined plate-like calcite crystals and to investigate the critical experimental parameters. Thus, in precipitation system c(NaHCO3) = c(CaCl2) = 0.1 mol dm−3, the influence of hydrodynamic parameters (mode of mixing of the reaction components) and a presence of lithium ions Li+ within a wide range of concentrations, 0.0 mol dm−3 < c(Li+) < 1.0 mol dm−3, have been studied. In addition, the kinetics of the solution mediated transformation of the initially formed metastable polymorph, va-terite, were followed in order to reproducibly describe the formation of stable calcite with expressed unstable morphology. The results indicate that the plate-like calcite is formed predominantly when the ultrasound irradiation is applied at c(Li+) ≥ 0.3 mol dm−3. On the other hand, when the magnetic and mechanical stirring are applied at higher Li+ concentrations, truncated rhombohedral crystals in a mixture with plate-like crystals are obtained. It was also found that the Li+ addition significantly prolonged the transformation, mainly by inhibiting the crystal growth of calcite.