Objectives. This study evaluated the role of endogenous dentin MMPs in auto-degradation of collagen fibrils within adhesive-bonded interfaces. The null hypotheses tested were that adhesive blends or chlorhexidine digluconate (CHX) application does not modify dentin MMPs activity and that CHX used as therapeutic primer does not improve the stability of adhesive interfaces over time. Methods. Zymograms of protein extracts from human dentin powder incubated with Adper Scotchbond 1XT (SB1XT) on untreated or 0.2-2% CHX-treated dentin were obtained to assay dentin MMPs activity. Microtensile bond strength and interfacial nanoleakage expression of SB1XT bonded interfaces ( with or without CHX pre-treatment for 30 s on the etched surface) were analyzed immediately and after 2 years of storage in artificial saliva at 37 degrees C. Results. Zymograms showed that application of SB1XT to human dentin powder increases MMP-2 activity, while CHX pre-treatment inhibited all dentin gelatinolytic activity, irrespective from the tested concentration. CHX significantly lowered the loss of bond strength and nanoleakage seen in acid-etched resin-bonded dentin artificially aged for 2 years. Significance. The study demonstrates the active role of SB1XT in dentin MMP-2 activation and the efficacy of CHX inhibition of MMPs even if used at low concentration (0.2%).
Chlorhexidine stabilizes the adhesive interface: A 2-year in vitro study.
BRESCHI, LORENZO;MAZZONI, ANNALISA;NATO, FERNANDO;RUGGERI, ALESSANDRA;
2010
Abstract
Objectives. This study evaluated the role of endogenous dentin MMPs in auto-degradation of collagen fibrils within adhesive-bonded interfaces. The null hypotheses tested were that adhesive blends or chlorhexidine digluconate (CHX) application does not modify dentin MMPs activity and that CHX used as therapeutic primer does not improve the stability of adhesive interfaces over time. Methods. Zymograms of protein extracts from human dentin powder incubated with Adper Scotchbond 1XT (SB1XT) on untreated or 0.2-2% CHX-treated dentin were obtained to assay dentin MMPs activity. Microtensile bond strength and interfacial nanoleakage expression of SB1XT bonded interfaces ( with or without CHX pre-treatment for 30 s on the etched surface) were analyzed immediately and after 2 years of storage in artificial saliva at 37 degrees C. Results. Zymograms showed that application of SB1XT to human dentin powder increases MMP-2 activity, while CHX pre-treatment inhibited all dentin gelatinolytic activity, irrespective from the tested concentration. CHX significantly lowered the loss of bond strength and nanoleakage seen in acid-etched resin-bonded dentin artificially aged for 2 years. Significance. The study demonstrates the active role of SB1XT in dentin MMP-2 activation and the efficacy of CHX inhibition of MMPs even if used at low concentration (0.2%).I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.