The research dealt with the correlation between fatigue life of a CFRP laminate composite and the thermal analysis information obtained during the fatigue tests. This study was done for two different lamination sequences and three different loading frequencies. The damage progression was evaluated also by stiffness reduction and hysteresis loop areas increase measurements. The thermal energy, that is the amount of mechanical energy dissipated in the form of heat, evaluated in the first few load cycles was found to be a good parameter to predict fatigue life.

G. Minak (2010). On the determination of the fatigue life of laminated graphite-epoxy composite by means of surface temperature measurement. JOURNAL OF COMPOSITE MATERIALS, 44, 1739-1752 [10.1177/0021998309359815].

On the determination of the fatigue life of laminated graphite-epoxy composite by means of surface temperature measurement

MINAK, GIANGIACOMO
2010

Abstract

The research dealt with the correlation between fatigue life of a CFRP laminate composite and the thermal analysis information obtained during the fatigue tests. This study was done for two different lamination sequences and three different loading frequencies. The damage progression was evaluated also by stiffness reduction and hysteresis loop areas increase measurements. The thermal energy, that is the amount of mechanical energy dissipated in the form of heat, evaluated in the first few load cycles was found to be a good parameter to predict fatigue life.
2010
G. Minak (2010). On the determination of the fatigue life of laminated graphite-epoxy composite by means of surface temperature measurement. JOURNAL OF COMPOSITE MATERIALS, 44, 1739-1752 [10.1177/0021998309359815].
G. Minak
File in questo prodotto:
Eventuali allegati, non sono esposti

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11585/80576
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 13
  • ???jsp.display-item.citation.isi??? 9
social impact