Anelastic Behavior of Small Dimensioned Aluminum / Enrico Gianfranco Campari, Stefano Amadori, Ennio Bonetti, Raffaele Berti, Roberto Montanari. - In: METALS. - ISSN 2075-4701. - ELETTRONICO. - 9:5(2019), pp. 549.1-549.9.
Titolo: | Anelastic Behavior of Small Dimensioned Aluminum |
Autore/i: | Enrico Gianfranco Campari; Stefano Amadori; Ennio Bonetti; Raffaele Berti; Roberto Montanari |
Autore/i Unibo: | |
Anno: | 2019 |
Rivista: | |
Digital Object Identifier (DOI): | http://dx.doi.org/10.3390/met9050549 |
Abstract: | Abstract: In the present research, results are presented regarding the anelasticity of 99.999% pure aluminum thin films, either deposited on silica substrates or as free-standing sheets obtained by cold rolling. Mechanical Spectroscopy (MS) tests, namely measurements of dynamic modulus and damping vs. temperature, were performed using a vibrating reed analyzer under vacuum. The damping vs. temperature curves of deposited films exhibit two peaks which tend to merge into a single peak as the specimen thickness increases above 0.2 μm. The thermally activated anelastic relaxation processes observed on free-standing films are strongly dependent on film thickness, and below a critical value of about 20 μm two anelastic relaxation peaks can be observed; both their activation energy and relaxation strength are affected by film thickness. These results, together with those observed on bulk specimens, are indicative of specific dislocation and grain boundary dynamics, constrained by the critical values of the ratio of film thickness to grain size. |
Data stato definitivo: | 2019-05-13T09:45:45Z |
Appare nelle tipologie: | 1.01 Articolo in rivista |
File in questo prodotto:
File | Descrizione | Tipo | Licenza | |
---|---|---|---|---|
metals-09-00549.pdf | Articolo in formato pdf | Versione (PDF) editoriale | Licenza per Accesso Aperto. Creative Commons Attribuzione (CCBY) | Open Access Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.