The spontaneous deposition of Pd directly onto Fecralloy foam substrates was investigated as a simple and convenient approach to the preparation of structured technological catalysts for environmental applications, avoiding issues typically encountered with washcoated systems. Characterization of freshly prepared catalysts included ion chromatography and ICP-MS, to assess the Pd loading, cyclic voltammetry, to estimate the Pd surface area, SEM-EDX, XRD and TPR/TPO. Cyclic voltammetry, SEM-EDX and XRD were performed also on reaction aged samples. CO and CH4catalytic oxidation under lean conditions were selected as test reactions occurring respectively in the low (100-300°C) and mid-high (300-600°C) temperature ranges. Pd-Fecralloy foam catalysts were found to guarantee good activity with an effective utilization of the noble metal content in spite of their relatively low Pd dispersion. © 2013 Elsevier B.V.
Cimino, S., Gerbasi, R., Lisi, L., Mancino, G., Musiani, M., Vázquez-Gómez, L., et al. (2013). Oxidation of CO and CH4on Pd-Fecralloy foam catalysts prepared by spontaneous deposition. CHEMICAL ENGINEERING JOURNAL, 230, 422-431 [10.1016/j.cej.2013.06.077].
Oxidation of CO and CH4on Pd-Fecralloy foam catalysts prepared by spontaneous deposition
Verlato, E.
2013
Abstract
The spontaneous deposition of Pd directly onto Fecralloy foam substrates was investigated as a simple and convenient approach to the preparation of structured technological catalysts for environmental applications, avoiding issues typically encountered with washcoated systems. Characterization of freshly prepared catalysts included ion chromatography and ICP-MS, to assess the Pd loading, cyclic voltammetry, to estimate the Pd surface area, SEM-EDX, XRD and TPR/TPO. Cyclic voltammetry, SEM-EDX and XRD were performed also on reaction aged samples. CO and CH4catalytic oxidation under lean conditions were selected as test reactions occurring respectively in the low (100-300°C) and mid-high (300-600°C) temperature ranges. Pd-Fecralloy foam catalysts were found to guarantee good activity with an effective utilization of the noble metal content in spite of their relatively low Pd dispersion. © 2013 Elsevier B.V.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.