Repair of ligaments and tendons requires scaffolds mimicking the spatial organisation of collagen in the natural tissue. Electrospinning is a promising technique to produce nanofibres of both resorbable and biostable polymers with desired structural and morphological features. The aim of this study was to perform high-resolution x-ray tomography (XCT) scans of bundles of Nylon6.6, pure PLLA and PLLA-Collagen blends, where the nanofibres were meant to have a predominant direction. Characterisation was carried out via a dedicated methodology to firmly hold the specimen during the scan and a workflow to quantify the directionality of the nanofibres in the bundle. XCT scans with 0.4 and 1.0 μm voxel size were successfully collected for all bundle compositions. Better image quality was achieved for those bundles formed by thicker nanofibres (i.e. 0.59 μm for pure PLLA), whereas partial volume effect was more pronounced for thinner nanofibres (i.e. 0.26 μm for Nylon6.6). As expected, the nanofibres had a predominant orientation along the axis of the bundles (more than 20% of the nanofibres within 3° and more than 60% within 18° from the bundle axis), with a Gaussian-like dispersion in the other directions. The directionality assessment was validated by comparison against a similar analysis performed on SEM images: the XCT analysis overestimated the amount of nanofibres very close to the bundle axis, especially for the materials with thinnest nanofibres, but adequately identified the amount of nanofibres within 12°.
Sensini, A., Cristofolini, L., Focarete, M., Belcari, J., Zucchelli, A., Kao, A., et al. (2018). High-resolution x-ray tomographic morphological characterisation of electrospun nanofibrous bundles for tendon and ligament regeneration and replacement. JOURNAL OF MICROSCOPY, 272(3), 196-206 [10.1111/jmi.12720].
High-resolution x-ray tomographic morphological characterisation of electrospun nanofibrous bundles for tendon and ligament regeneration and replacement
Sensini, A.Primo
;Cristofolini, L.
Secondo
;Focarete, M. L.;Zucchelli, A.;
2018
Abstract
Repair of ligaments and tendons requires scaffolds mimicking the spatial organisation of collagen in the natural tissue. Electrospinning is a promising technique to produce nanofibres of both resorbable and biostable polymers with desired structural and morphological features. The aim of this study was to perform high-resolution x-ray tomography (XCT) scans of bundles of Nylon6.6, pure PLLA and PLLA-Collagen blends, where the nanofibres were meant to have a predominant direction. Characterisation was carried out via a dedicated methodology to firmly hold the specimen during the scan and a workflow to quantify the directionality of the nanofibres in the bundle. XCT scans with 0.4 and 1.0 μm voxel size were successfully collected for all bundle compositions. Better image quality was achieved for those bundles formed by thicker nanofibres (i.e. 0.59 μm for pure PLLA), whereas partial volume effect was more pronounced for thinner nanofibres (i.e. 0.26 μm for Nylon6.6). As expected, the nanofibres had a predominant orientation along the axis of the bundles (more than 20% of the nanofibres within 3° and more than 60% within 18° from the bundle axis), with a Gaussian-like dispersion in the other directions. The directionality assessment was validated by comparison against a similar analysis performed on SEM images: the XCT analysis overestimated the amount of nanofibres very close to the bundle axis, especially for the materials with thinnest nanofibres, but adequately identified the amount of nanofibres within 12°.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.