IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishPolyphase boride coatings constituted by an inner layer of Fe2B and an outer layer of FeB were thermochemically grown on iron and medium carbon steel by a pack cementation process. The tribological behaviour of borided samples was investigated under both sliding and abrasion testing conditions. Considerably different values of wear rate were found in different regions of the coatings. The differences were explained on the basis of the crystallographic order of iron borides. The resistance to both types of wear was initially poor due to the presence on the coatings of a thin, friable layer constituted by disordered crystals. Then the resistance increased to a maximum value in regions constituted by compact, highly ordered crystals of Fe2B. The resistance to dry sliding of borided samples was better than that displayed by samples submitted to alternative surface treatments (e.g. gas nitriding) and lower that that measured for a WC-Co hard metal coating.
| Titolo: | Sliding and abrasive wear behaviour of boride coatings | |
| Autore/i: | MARTINI, CARLA; PALOMBARINI, GIUSEPPE; POLI G.; PRANDSTRALLER, DARIA | |
| Autore/i Unibo: | ||
| Anno: | 2004 | |
| Rivista: | ||
| Digital Object Identifier (DOI): | http://dx.doi.org/10.1016/j.wear.2003.10.003 | |
| Abstract: | Polyphase boride coatings constituted by an inner layer of Fe2B and an outer layer of FeB were thermochemically grown on iron and medium carbon steel by a pack cementation process. The tribological behaviour of borided samples was investigated under both sliding and abrasion testing conditions. Considerably different values of wear rate were found in different regions of the coatings. The differences were explained on the basis of the crystallographic order of iron borides. The resistance to both types of wear was initially poor due to the presence on the coatings of a thin, friable layer constituted by disordered crystals. Then the resistance increased to a maximum value in regions constituted by compact, highly ordered crystals of Fe2B. The resistance to dry sliding of borided samples was better than that displayed by samples submitted to alternative surface treatments (e.g. gas nitriding) and lower that that measured for a WC-Co hard metal coating. | |
| Data prodotto definitivo in UGOV: | 2005-10-18 11:32:01 | |
| Data stato definitivo: | 2019-02-27T13:21:52Z | |
| Appare nelle tipologie: | 1.01 Articolo in rivista |
File in questo prodotto:
Copyright © 2022