The melting behavior and the crystallization kinetics of block poly(butylene/thiodiethylene succinate) copolymers (PBSPTDGS) with identical chemical composition (i.e., BS:TDGS = 50:50 mol %) were investigated by means of differential scanning calorimetry. Multiple endotherms were evidenced in PBSPTDGS samples, because of melting and recrystallization processes, similar to poly(butylene succinate) (PBS). By applying the Hoffman–Weeks’ method, the Tm of the copolymers was derived. The isothermal crystallization kinetics was analyzed according to the Avrami’s treatment. The copolymer with long PBS blocks (PBSPTDGS15) is characterized by a very similar behavior with respect to pure PBS, indicating that PBS macromolecular folding is not affected by the presence of noncrystallizable thiodiethylene succinate blocks. In all the other cases, the overall crystallization rate was found to decrease as the block length is decreased, even though the work of chain folding, derived on the basis of Hoffman–Lauritzen nucleation theory, also decreased with the block length.

M. Soccio, N. Lotti, A. Munari (2013). Influence of block length on crystallization kinetics and melting behavior of poly(butylene/thiodiethylene succinate) block copolymers. JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 114(2), 677-688 [10.1007/s10973-013-3040-4].

Influence of block length on crystallization kinetics and melting behavior of poly(butylene/thiodiethylene succinate) block copolymers

M. Soccio;LOTTI, NADIA;MUNARI, ANDREA
2013

Abstract

The melting behavior and the crystallization kinetics of block poly(butylene/thiodiethylene succinate) copolymers (PBSPTDGS) with identical chemical composition (i.e., BS:TDGS = 50:50 mol %) were investigated by means of differential scanning calorimetry. Multiple endotherms were evidenced in PBSPTDGS samples, because of melting and recrystallization processes, similar to poly(butylene succinate) (PBS). By applying the Hoffman–Weeks’ method, the Tm of the copolymers was derived. The isothermal crystallization kinetics was analyzed according to the Avrami’s treatment. The copolymer with long PBS blocks (PBSPTDGS15) is characterized by a very similar behavior with respect to pure PBS, indicating that PBS macromolecular folding is not affected by the presence of noncrystallizable thiodiethylene succinate blocks. In all the other cases, the overall crystallization rate was found to decrease as the block length is decreased, even though the work of chain folding, derived on the basis of Hoffman–Lauritzen nucleation theory, also decreased with the block length.
2013
M. Soccio, N. Lotti, A. Munari (2013). Influence of block length on crystallization kinetics and melting behavior of poly(butylene/thiodiethylene succinate) block copolymers. JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 114(2), 677-688 [10.1007/s10973-013-3040-4].
M. Soccio; N. Lotti; A. Munari
File in questo prodotto:
Eventuali allegati, non sono esposti

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11585/191567
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 11
social impact