Abstract OBJECTIVES: To evaluate the influence of the ferrule effect (1) and the fibre-post placement (2) on the fracture resistance of endodontically treated teeth subjected to cyclic fatigue loading. METHODS: 40 extracted single-rooted upper pre-molars were sectioned at the CEJ (groups a and b) or 2mm above the CEJ (groups c and d), and subsequently endodontically treated. After 24-h water storage at 37°C, specimens were restored according to four build-up approaches (n=10 per group): (a) NF-NP (no ferrule, no post), (b) NF-P (no ferrule, fibre-post), (c) F-NP (ferrule, no post) and (d) F-P (ferrule, fibre post). RelyX Posts (3M-ESPE) were used in groups NF-P and F-P, and were cemented with Panavia F 2.0 (Kuraray). A standardized composite core was built, after which specimens were restored with an all-ceramic crown (IPS Empress CAD, Ivoclar-Vivadent) Specimens were fatigued by exposure to 1,200,000 cycles using a chewing simulator (Willytech). All specimens that survived fatigue loading were fractured using a universal loading device (Micro-Tester, Instron). A two-way analysis of variance was used to determine the statistical significance of the factors ferrule and post on fracture resistance. RESULTS: Only one NF-NP specimen failed under fatigue. The ferrule effect significantly enhanced the fracture resistance of the restored teeth, regardless the use of a post (p=0.003). F-NP obtained the highest fracture resistance (758.52±121.89N), which was not significantly different from F-P (647.58±132.95N); NF-NP presented the lowest fracture resistance (361.52±151.69N). For all groups, only 'repairable' failures were recorded. CONCLUSIONS: Avoiding extra-removal of sound tooth structure, rather than placing a fibre post, can protect endodontically treated teeth against catastrophic failure. However, when any ferrule can be preserved, a fibre-post may improve the retention and fatigue resistance of the restoration.
Effect of ferrule and post placement on fracture resistance of endodontically treated teeth after fatigue loading / Zicari F; Van Meerbeek B; Scotti R; Naert I.. - In: JOURNAL OF DENTISTRY. - ISSN 0300-5712. - STAMPA. - 41:(2013), pp. 207-215. [10.1016/j.jdent.2012.10.004]
Effect of ferrule and post placement on fracture resistance of endodontically treated teeth after fatigue loading.
ZICARI, FRANCESCA;SCOTTI, ROBERTO;
2013
Abstract
Abstract OBJECTIVES: To evaluate the influence of the ferrule effect (1) and the fibre-post placement (2) on the fracture resistance of endodontically treated teeth subjected to cyclic fatigue loading. METHODS: 40 extracted single-rooted upper pre-molars were sectioned at the CEJ (groups a and b) or 2mm above the CEJ (groups c and d), and subsequently endodontically treated. After 24-h water storage at 37°C, specimens were restored according to four build-up approaches (n=10 per group): (a) NF-NP (no ferrule, no post), (b) NF-P (no ferrule, fibre-post), (c) F-NP (ferrule, no post) and (d) F-P (ferrule, fibre post). RelyX Posts (3M-ESPE) were used in groups NF-P and F-P, and were cemented with Panavia F 2.0 (Kuraray). A standardized composite core was built, after which specimens were restored with an all-ceramic crown (IPS Empress CAD, Ivoclar-Vivadent) Specimens were fatigued by exposure to 1,200,000 cycles using a chewing simulator (Willytech). All specimens that survived fatigue loading were fractured using a universal loading device (Micro-Tester, Instron). A two-way analysis of variance was used to determine the statistical significance of the factors ferrule and post on fracture resistance. RESULTS: Only one NF-NP specimen failed under fatigue. The ferrule effect significantly enhanced the fracture resistance of the restored teeth, regardless the use of a post (p=0.003). F-NP obtained the highest fracture resistance (758.52±121.89N), which was not significantly different from F-P (647.58±132.95N); NF-NP presented the lowest fracture resistance (361.52±151.69N). For all groups, only 'repairable' failures were recorded. CONCLUSIONS: Avoiding extra-removal of sound tooth structure, rather than placing a fibre post, can protect endodontically treated teeth against catastrophic failure. However, when any ferrule can be preserved, a fibre-post may improve the retention and fatigue resistance of the restoration.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.