Two types of model cables having different cross-linked polyethylene (XLPE) materials are investigated in this paper. One material is a standard XLPE homopolymer; the other is high productivity XLPE compound. Electric properties of these cables were studied and compared under AC and DC field, respectively. In particular, AC voltage endurance was evaluated by means of an experimental system developed for ageing and life tests in dry condition. Additional information on the charge trapping phenomenology under DC field was obtained from the space charge measurements.

L. Wang, D. Fabiani, G. C. Montanari, F. Palmieri, U.H. Nilsson (2011). Electric Properties of XLPE Model Cables under AC and DC Field at Various Temperatures. PARIS : SEE.

Electric Properties of XLPE Model Cables under AC and DC Field at Various Temperatures

FABIANI, DAVIDE;MONTANARI, GIAN CARLO;
2011

Abstract

Two types of model cables having different cross-linked polyethylene (XLPE) materials are investigated in this paper. One material is a standard XLPE homopolymer; the other is high productivity XLPE compound. Electric properties of these cables were studied and compared under AC and DC field, respectively. In particular, AC voltage endurance was evaluated by means of an experimental system developed for ageing and life tests in dry condition. Additional information on the charge trapping phenomenology under DC field was obtained from the space charge measurements.
2011
Proceedings of JICABLE'11
10
16
L. Wang, D. Fabiani, G. C. Montanari, F. Palmieri, U.H. Nilsson (2011). Electric Properties of XLPE Model Cables under AC and DC Field at Various Temperatures. PARIS : SEE.
L. Wang; D. Fabiani; G. C. Montanari; F. Palmieri; U.H. Nilsson
File in questo prodotto:
Eventuali allegati, non sono esposti

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11585/131162
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact