In this paper the first example of using C-dots (CDs) as sensing nanomaterial for monitoring low concentrations of NO2 in ambient air is reported. In the logic to support a green circular economy, CDs were prepared from a natural low cost precursor consisting in olive solid waste (OSW) by a simple pyrolysis process combined with chemical oxidation. Characterization data showed the formation of spherical CDs with dimensions in the narrow size range from 0.5 to 5 nm and charged with functional groups (COO- (carboxylate), C-O-C (epoxide) and C-OH (hydroxyl) imprinting excellent water colloidal dispersion. The nanomaterial was used to fabricate and test a conductometric gas sensor (CDs-sensor) that was found to exhibit excellent performances in terms of high and selective response to sub-ppm concentration of NO2 at low temperature (150 °C), low limit of detection (LOD) of 50 ppb, good reproducibility and stability over use and aging. To the best of our knowledge, this is the first example reported in the literature of CDs high performances gas sensing material. Results here presented pave the way for a new class of a carbon nanomaterial for gas sensing to be applied in the field of environmental monitoring.
Sawalha, S., Moulaee, K., Nocito, G., Silvestri, A., Petralia, S., Prato, M., et al. (2021). Carbon-dots conductometric sensor for high performance gas sensing. CARBON TRENDS, 5, 100105-100105 [10.1016/j.cartre.2021.100105].
Carbon-dots conductometric sensor for high performance gas sensing
Sabrina Conoci;
2021
Abstract
In this paper the first example of using C-dots (CDs) as sensing nanomaterial for monitoring low concentrations of NO2 in ambient air is reported. In the logic to support a green circular economy, CDs were prepared from a natural low cost precursor consisting in olive solid waste (OSW) by a simple pyrolysis process combined with chemical oxidation. Characterization data showed the formation of spherical CDs with dimensions in the narrow size range from 0.5 to 5 nm and charged with functional groups (COO- (carboxylate), C-O-C (epoxide) and C-OH (hydroxyl) imprinting excellent water colloidal dispersion. The nanomaterial was used to fabricate and test a conductometric gas sensor (CDs-sensor) that was found to exhibit excellent performances in terms of high and selective response to sub-ppm concentration of NO2 at low temperature (150 °C), low limit of detection (LOD) of 50 ppb, good reproducibility and stability over use and aging. To the best of our knowledge, this is the first example reported in the literature of CDs high performances gas sensing material. Results here presented pave the way for a new class of a carbon nanomaterial for gas sensing to be applied in the field of environmental monitoring.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.