Room-temperature photorefractivity without prepoling was demonstrated in polymers and copolymers with a glass transition temperature well above 100 °C. The compounds used are multifunctional sidechain polymers exhibiting chiral, semiconducting, photochromic, and nonlinear optical (azoaromatic moieties) properties. The photorefractive performance was linked to the reorientational effect of the photogenerated space-charge field, which well below the glass transition temperature can be active in the presence of the conformational mobility achieved via the trans-cis light-induced isomerization. The grating build-up time, which is long at λ ) 633 nm (with a time constant τ ≈ 500-1000 s) decreases by 2 orders of magnitude at λ ) 532 nm, where absorption is higher.

High Tg azopolymers for Photorefractive applications

ANGIOLINI, LUIGI;GIORGINI, LORIS;
2009

Abstract

Room-temperature photorefractivity without prepoling was demonstrated in polymers and copolymers with a glass transition temperature well above 100 °C. The compounds used are multifunctional sidechain polymers exhibiting chiral, semiconducting, photochromic, and nonlinear optical (azoaromatic moieties) properties. The photorefractive performance was linked to the reorientational effect of the photogenerated space-charge field, which well below the glass transition temperature can be active in the presence of the conformational mobility achieved via the trans-cis light-induced isomerization. The grating build-up time, which is long at λ ) 633 nm (with a time constant τ ≈ 500-1000 s) decreases by 2 orders of magnitude at λ ) 532 nm, where absorption is higher.
2009
L. Angiolini; L. Giorgini; A. Golemme; Q. Lhi; F. Mauriello; R. Termine
File in questo prodotto:
Eventuali allegati, non sono esposti

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11585/77010
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 23
  • ???jsp.display-item.citation.isi??? 21
social impact