In order to bring the treatment of historical bronze monuments in line with proper engineering practice and cultural heritage regulations, the standardisation of artificially aged surfaces that are comparable with natural ones is still to take place. In this aim, this investigation reports a comparative study of corroded quaternary bronze samples produced by accelerated ageing tests, simulating the unsheltered and sheltered exposure conditions mainly affecting outdoor bronze monuments. The effects of run off in a dropping test (unsheltered simulation) and the exposure to stagnant acid rain in a wet & dry test (sheltered simulation) on a bronze surface were studied. A multi-analytical approach was performed including conventional analytical methods, such as a microscopy examination coupled with elemental and structural analyses of the surface. In addition, a focused ion beam (FIB) was used to produce cross-sections in the size range up to a few tens of nanometres. It is evidenced that the corrosion layers, forming a nano-porous structure, are linked to a decuprification process marked by the preferential dissolution of Cu and Zn and the formation of a SnO species network within the barrier layer. A correlation between the tin content of the alloy and the corrosion amplitude is shown: the anodic areas are related to the lowest tin-content part of the alpha phase (in the centre of the dendrite), while the eutectoid areas (including the delta phase) are cathodic and therefore not attacked. The corroded samples artificially aged are well representative of natural corrosion structures observed on outdoor bronzes.

Characterisation of typical patinas simulating bronze corrosion in outdoor conditions / Masi, G.; Esvan, J.; Josse, C.; Chiavari, C.; Bernardi, E.; Martini, C.; Bignozzi, M. C.; Gartner, N.; Kosec, T.; Robbiola, L.. - In: MATERIALS CHEMISTRY AND PHYSICS. - ISSN 0254-0584. - STAMPA. - 200:(2017), pp. 308-321. [10.1016/j.matchemphys.2017.07.091]

Characterisation of typical patinas simulating bronze corrosion in outdoor conditions

MASI, GIULIA;CHIAVARI, CRISTINA;BERNARDI, ELENA;MARTINI, CARLA;BIGNOZZI, MARIA;
2017

Abstract

In order to bring the treatment of historical bronze monuments in line with proper engineering practice and cultural heritage regulations, the standardisation of artificially aged surfaces that are comparable with natural ones is still to take place. In this aim, this investigation reports a comparative study of corroded quaternary bronze samples produced by accelerated ageing tests, simulating the unsheltered and sheltered exposure conditions mainly affecting outdoor bronze monuments. The effects of run off in a dropping test (unsheltered simulation) and the exposure to stagnant acid rain in a wet & dry test (sheltered simulation) on a bronze surface were studied. A multi-analytical approach was performed including conventional analytical methods, such as a microscopy examination coupled with elemental and structural analyses of the surface. In addition, a focused ion beam (FIB) was used to produce cross-sections in the size range up to a few tens of nanometres. It is evidenced that the corrosion layers, forming a nano-porous structure, are linked to a decuprification process marked by the preferential dissolution of Cu and Zn and the formation of a SnO species network within the barrier layer. A correlation between the tin content of the alloy and the corrosion amplitude is shown: the anodic areas are related to the lowest tin-content part of the alpha phase (in the centre of the dendrite), while the eutectoid areas (including the delta phase) are cathodic and therefore not attacked. The corroded samples artificially aged are well representative of natural corrosion structures observed on outdoor bronzes.
2017
Characterisation of typical patinas simulating bronze corrosion in outdoor conditions / Masi, G.; Esvan, J.; Josse, C.; Chiavari, C.; Bernardi, E.; Martini, C.; Bignozzi, M. C.; Gartner, N.; Kosec, T.; Robbiola, L.. - In: MATERIALS CHEMISTRY AND PHYSICS. - ISSN 0254-0584. - STAMPA. - 200:(2017), pp. 308-321. [10.1016/j.matchemphys.2017.07.091]
Masi, G.; Esvan, J.; Josse, C.; Chiavari, C.; Bernardi, E.; Martini, C.; Bignozzi, M. C.; Gartner, N.; Kosec, T.; Robbiola, L.
File in questo prodotto:
File Dimensione Formato  
Accepted Manuscript_MatChemPhys17.pdf

accesso aperto

Tipo: Postprint
Licenza: Licenza per Accesso Aperto. Creative Commons Attribuzione - Non commerciale - Non opere derivate (CCBYNCND)
Dimensione 2.23 MB
Formato Adobe PDF
2.23 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11585/609736
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 44
  • ???jsp.display-item.citation.isi??? 42
social impact